Description Carbon Nanotube Masterbatches CNT-PA6-15 Our carbon nanotube masterbatches CNT-PA6-15 use our industrial grade multi walled carbon nanotubes. This product has a 15% CNTs loading ratio. The CNT-PA6-15 material can be used with 3D printers, injection molders, & extruders. Once received, you simply let it down and run it in your equipment. Sold by the kilogram Product Code Matrix Resin Matrix Resin Loading CNTs Code CNTs Loading CNT-PA6-15 PA6 85wt% IGMWNTs 20-40nm 15wt% CNT-PA6- 15 was dispersed in PA6 using twin-screw extruder, the pellets are made by injection molding. Volume and surface resistivity were measured by high insulation resistance instrument ZC-90D（IEC 60093-1980, the test voltage is 100V）. CNTs Loading（wt%） 2 3 Volume Resistivity (ohm.cm) 2.2×1012 6.3×107 Surface Resistivity (ohm) 1.6×1013 2.7×107 CNT-PA6-15 was diluted by PA6 using twin-screw extruder, then the specimens were made by injection molding. The standard of mechanical property of specimens was ISO 527, ISO 180 and ISO 178. CNTs Loading（wt%） 0（Pure PA6） 3 Tensile Strength（MPa） 62.6 71.4 Stain at break（%） 52.9 17.8 Izod Notched Impact Strength（KJ/m2） 7.9 4.1 Flexural Strength（MPa） 77.5 82.6 Flexural Modulus（MPa） 1696 1940