Description Carbon Nanotube Masterbatches CNT-ABS-10 Our carbon nanotube masterbatches CNT-ABS-10 usees our industrial grade multi walled carbon nanotubes. This product has a 15% CNTs loading ratio. The CNT-ABS-10 material can be used with 3D printers, injection molders, & extruders. Once received, you simply let it down and run it in your equipment. Sold by the kilogram Product Code Matrix Resin Matrix Resin Loading CNTs Code CNTs Loading Resistivity (four probe method) CNT/ABS ABS 757 90wt% IGMWNTS 10wt% 8 ohm.cm CNTs were dispersed in ABS using twin-screw extruder, then the specimens were made by compression molding. Volume and surface resistivity were measured by high insulation resistance instrument ZC-90D（IEC 60093-1980, the test voltage is 100V). CNTs Loading（wt%） 2.5 Volume Resistivity (ohm.cm) 1.1×109 Surface Resistivity (ohm) 3.2×107 CNTs were dispersed in ABS using twin-screw extruder, then the specimens were made by injection molding. The standard of mechanical property of specimens was ISO 527, ISO 180 and ISO 178. CNTs Loading（wt%） 0（Neat ABS） 2.5 Tensile Strength（MPa） 49.9 49.7 Stain at break（%） 11 6 Izod Notched Impact Strength（KJ/m2） 15.4 7.1 Flexural Strength（MPa） 78 81 Flexural Modulus（MPa） 2689 2888 Melt Index （g/10min，5Kg/220℃） 19 12.8